you could try a mixture of 2 parts silica to one part plaster. Its what I use to make glass slumping molds. You would have to heat it very slowly in the kiln very slowly until all the water was gone about 1100 degrees before adding glass. It would be a right pain removing from the inside of your glass form when finished.