[beadforever]

I guess I did not make it clear what I am referring to or see as a possible problem . What I mean is even if one batch anneals the beads properly if the glass form stress in it will that stress still remain even after a batch anneal as stress is formed through the cooling stage whether the glass cooled in a kin , fiber blanket, or annealing bubbles . annealing would not remove that stress in the glass only stop stress form forming if done properly. Would my assumption be true ??