7.1%? well I never. But this is the place to come with questions. Any scientific reasons behind that, Larry? Just wondering. I would think that if all I am using is 96coe, then there should not be an issue. Or it would be user error, looking at my bead too long and getting it too cool. But I have diligently tried to make these beads with those warnings in mind and have still gotten cracks. Have another batch to look at this morning..... thanks eveyone for your comments. This is my first posting, and it is gratifying to get input from people in this community.
|