It could be something like the thickness of your wire compared to the mass of glass.
But if you think they're OK, try putting them in the kiln directly. That way you'll know for sure if it's the wire/glass ratio, a direct annealing issue, or what the problem might be.
Different wires are good to try too. Nichrome, kanthal, brass...