Quote:
Originally Posted by laserglass View Post
i'm sorry, but your poll does not make any sense. annealing is a procedure, with various ramp rates and temperatures. the length of time you hold the glass (T3) depends upon how thick it is. see chart below.
i'm glad this subject came up. i'm using and adapted version of an annealing schedule i found on WC but i have no idea if it's accurate or not based on the size of my beads. My beads are usually at least 1.5" in length/width but generally not very thick...

and Mark, (even tho i wish i could) i have absolutely no idea how to interpret your chart...
__________________
Evelyn - Carlisle Lucio w/ 8lpm EX-15
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.


To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.

To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.

To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.


To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.

Give ideas away - there are new ones underneath... Diane Vreeland
Reply With Quote