Quote:
Originally Posted by bepnewt
^^^ This ^^^
|
^^^ That ^^^
as a general rule of thumb, if the wallthickness is thinner, it'll less likely to break due to stress without annealing, because of the lower mass and and it will have less stress due to the way the heat differential occurs in thinner glass (as opposed to heavy walled glass). See if medium or lightwall is suitable. I think it probably is in such a small piece.