I am almost there, I played a bit last night. Just like everyone else, I thought I had got a consistent copper, but after they came out of the kiln, not all of them were that colours. I think the bead I had the most success with was one that I let cool completely before re-introducing it to a bushy reduction flame. I would let it cool before each re-introduction, it took ages.
Gonna try with some spacers tomorrow