Bullseye glass cracking issues
Are there some bullseye glasses that don't play well together? I had about 5 of them all with the crack down the middle even though I heated them really well before going into the kiln. The issue I'm thinking may be the clear/white rod but not sure. I also had some white heart beads with white in the middle incased in pale yellow.
Could it be the annealing shedule? I have always annealed at the same temperature as moretti.
Any suggestions would be awesome!