Quote:
Originally Posted by SuzyQ
You just answered your own question, lol. Work it higher in the flame. I would guess you are working too hot. You can get away with it for a lot of glasses but some just want you to treat them right
|
Actually, what I found was that if I worked HOTTER it stopped pitting, not the other way around, which doesn't make any sense.
I'm trying to see if anyone else has worked with Azure enough to have come up with a more logical answer.