Quote:
Originally Posted by Fire Warped Glass
Thanks for all the info BEP and KJohn. Just one more question. If I found an oxycon that had been used medically, could I go ahead and use it for glass, or would it have to be converted somehow?
|
No issue at all. Are you willing to sacrifice performance for this change? Only thing you can be sure of is that you will be somewhat oxygen deprived and that if you use boro silver striking colors you will most likely have problems.