Since it is happening right by the hole/mandrel it may not have enough heat, and/or thickness there. I can't remember the exact rule, but I think it was needs to be thicker than the mandrel itself on each side around the mandrel itself. So particularly with a lentil where it narrows at the edges it would be more likely to develop a running crack. Just a thought.