I also read somewhere that they crack easily in the flame possibly from not being annealed? That's a problem I had... Would it help to batch anneal them first and then heat them up in the bead door so that they're hot going In the flame? Would that help?
__________________
Gabi
Pincel de Fuego
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. / To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. / To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|