No. As the others above have said, if the beads are annealed and cooled properly, it doesn't matter what stress might have previously been in them. They will now be properly annealed, assuming they didn't crack while being heated to annealing temp. (Seems redundant, but that appears to be what you're asking.)

On the other hand, if they were made with incompatible glasses, it doesn't matter how much annealing they get. There will always be residual stress in them.