Brass press verses graphite press?
Anyone have any information which is easier to use or makes a better bead. Wanting a heart press and cannot decide which one brass or graphite. I have not tried any graphite presses.
|
2017-03-19, 5:07pm
|
Senior Member
|
|
Join Date: Feb 02, 2010
Posts: 3,382
|
|
Graphite isn't going to heat up and stick to your glass but it will eventually start to degrade around the edges and is more prone to damage than brass. Graphite is wayyy less expensive than brass. However, if you're not doing production work, I'd go with graphite. I have graphite I've used for almost a decade, doing occasional torching, that's almost as good as new.
__________________
ESC
Soft glass on a Minor/concentrator since 1996
|
2017-03-20, 9:59am
|
|
MacGalver
|
|
Join Date: Oct 15, 2006
Posts: 9,927
|
|
I prefer graphite to brass because it is less "grabby". It's hard to explain, but the brass sucks the heat out of the glass so quickly that it kind of feels dead to me after being pressed. It's not something you can see, but there's a feel to it that I personally dislike. Your mileage may vary! Keep in mind, I am one of those people who feels the glass "sigh" sometimes ~ it's just the way my brain works......
__________________
Jo
Frit Diva website To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2017-03-20, 10:06am
|
|
Senior Member
|
|
Join Date: Aug 27, 2005
Location: Florida
Posts: 2,186
|
|
As a press I think brass is more durable. Graphite and brass work differently with glass. Glass slides over graphite without any pulling. Brass grips the glass. For presses this is not a problem as long as it is made well without any undercuts.
__________________
Heather Ferman Web site: To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
Viking knit End Caps for sale:
[/url]https://heatherferman.etsy.com[/url]
|
2017-03-20, 11:34am
|
|
Phill
|
|
Join Date: Mar 21, 2009
Location: Winnebago, MN
Posts: 2,489
|
|
Another thought is that graphite has dozens of various grades and can come in some really poor qualities that would take a good deal of self educating to get knowledgeable on.
Brass only comes in three or four formulations and so can be relied on for getting what you are paying for.
We do have several commercial vendors here that can be depended on here on the LE forum that produce high quality graphite tools.
Graphite is made from carbon and can burn off if exposed to direct flame and is also subject to some wear over time.
Brass has much less of a problem with wear.
Using molds of any sort is going to involve learning heat control in glass and it must also be remembered that molds are more effectively used to 'guide' glass when it is hot enough to be in a plastic state and less as a method of 'forcing' the glass into a form like a glass bottling plant or a molten glass 'hot shop' where liquefied glass is kept in a kiln.
__________________
The Zombie Apocalypse is Upon Us.
|
2017-03-22, 6:52am
|
|
Member
|
|
Join Date: Feb 06, 2015
Location: US East Coast
Posts: 64
|
|
Personally I prefer brass, especially when I'm working with very stiff glass. Brass seems to retain it's resale value better also, if you aren't sure you're going to love the press.
|
2017-03-22, 8:55am
|
|
professional gimme fiver
|
|
Join Date: Feb 12, 2007
Location: Lancaster, PA
Posts: 1,207
|
|
I don't like brass tools as much as graphite. Brass is too cold. My personal preference.
__________________
Alexis
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2017-03-22, 12:42pm
|
|
Salt Box Beads
|
|
Join Date: Oct 23, 2005
Location: Heading to Paradise
Posts: 4,161
|
|
Prefer graphite here too.
|
2017-03-23, 12:04pm
|
|
Senior Member
|
|
Join Date: Sep 14, 2005
Location: Woodburn, OR
Posts: 1,854
|
|
It's graphite for my choice, I have both graphite and brass presses/rollers. I seem to grab the graphite presses before the brass ones when I am working
Liz R
__________________
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
MADE IN THE U.S.A.
Lead me not into temptation, Oh hell follow me I know a short cut
|
2017-03-26, 3:23am
|
|
Senior Member
|
|
Join Date: Aug 09, 2008
Location: Grand Rapids, MI
Posts: 1,086
|
|
I have both as well, I like them both, so far the graphite presses I haven't had any problems with. I usually buy presses based on the shape rather than material. I have one perlenpress graphite press that I really like and use a lot that is not offered in brass.
|
Currently Active Users Viewing This Thread: 1 (0 members and 1 guests)
|
|
Posting Rules
|
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts
HTML code is Off
|
|
|
All times are GMT -7. The time now is 2:09pm.
|