Using vintage glass components
I have quite a few vintage Czech glass components, both beads and cabochons. This summer I will go back to the Czech beadtown of Jablonec, and was wondering if anyone knows if they can be used for lampwork. With using them, I mean melting the glass into newly made beads. So I guess the question is: does anyone know if the COE of pressing rods is the same as lampwork rods?
They are made from pressing rods, probably made by Jablonex, now Ornela.
In the images you see a set of 'dragon's breath' vintage cabs. I don't think these would keep their appearance when reheated, but I might give it a try.
The second image shows uranium glass, of which I also have quite a bit of, both in beads and a few pressing rods. Any experience with this type of glass?
|
2013-03-29, 7:50am
|
|
Loving learning
|
|
Join Date: Oct 11, 2010
Location: Florida
Posts: 11,654
|
|
Just curious, but could you pull a stringer with it and a rod of a known
coe as in the compatibility test? (one side one, the other side the other, straight pull to see if it bends after pulling or stays straight)
__________________
My current "hot" fantasy involves a senior discount on glass & tools!
|
2013-03-29, 7:52am
|
Senior Member
|
|
Join Date: Mar 25, 2013
Posts: 327
|
|
That would be a good idea. I could just chip off some piece of a pressing rod and test it like that. It will have to wait a few weeks. Do not have my equipment set up at home yet. Also, I am still completely new to all of this. Just trying to learn a lot before I dive in completely.
|
2013-03-29, 8:17am
|
|
Senior Member
|
|
Join Date: Oct 02, 2007
Location: Toronto
Posts: 441
|
|
I've been told that the pressing rods are all different coe's, so they don't blend them unless they know they know they will 'fit'
Laurie
__________________
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2013-03-29, 9:35am
|
|
Lampworkaholic!
|
|
Join Date: Apr 22, 2008
Location: Cornelius, NC - because weather
Posts: 5,158
|
|
You might contact Preciosa-Ornela, since the do make Lampwork cane as well as beads.
http://www.preciosa-ornela.com/
__________________
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
"And all will turn to silver glass, a light on the water, grey ships pass into the west." Annie Lennox
|
2013-03-29, 6:36pm
|
|
Artistically Absorbed
|
|
Join Date: Jul 27, 2007
Location: Emerald City
Posts: 546
|
|
I have played around a little with Czech pressed beads, I used it with 104...they are still intact, but it was a surface application. They may all vary in COE...it never hurts experiment I say. I waste glass sometimes with beads I don't like after they are done, so what's a little more for experimentation sake?
__________________
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. Believe in Yourself and Anything is Possible! To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. SRA Artist A64
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2013-03-29, 8:01pm
|
|
honorary bead lady
|
|
Join Date: Jan 14, 2008
Location: Mostly the doghouse
Posts: 5,180
|
|
a while back i shot off an e-mail to Preciosa-Ornela about their coe and was told their "Lead (composite) rods with COE 96 Leadfree rods with COE 112"
__________________
David To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2013-03-30, 1:43pm
|
Senior Member
|
|
Join Date: Mar 25, 2013
Posts: 327
|
|
That is good to know, and I agree that experimentation is always good.
I'll have a go and document it.
|
Currently Active Users Viewing This Thread: 1 (0 members and 1 guests)
|
|
Posting Rules
|
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts
HTML code is Off
|
|
|
All times are GMT -7. The time now is 10:01am.
|