Encasing & Puckered end Help
Hi Everyone,
I have been encasing a lot of round beads, using a brass shaper and a stainless steel poker with a half rounded head (from Corina's poker set) to move glass towards the mandrel. Mainly I try to use as much gravity as possible to move the glass to get a puckered hole.
My problem now is that sometimes, I may make one wrong move and a tiny bit of glass may hit the mandrel around the hole. Is there any way back?? Am I doomed??? I haven't been able to find a way to fix my problem. If I add more glass to compensate that seems to make matters worse.
Ugh, it's tough when you all know you can spend an hour or more on a bead and then are on your final encasing.... and BAM, I seem to be screwing it up!
Any thoughts?
__________________
Happy Torching! Julie
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
~
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
~
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
~
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
~
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2013-03-16, 7:13pm
|
 |
Jacqueline Parkes
|
|
Join Date: Nov 04, 2005
Location: Vancouver, Canada
Posts: 4,497
|
|
I know this isn't the answer you want but I just use those beads to go into pendants with a nice beadcap on top. Then the hole is concealed.
__________________
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2013-03-16, 7:30pm
|
|
Senior Member
|
|
Join Date: Nov 22, 2012
Location: Eastern Shore Maryland
Posts: 958
|
|
Quote:
Originally Posted by gemsinbloom
I know this isn't the answer you want but I just use those beads to go into pendants with a nice beadcap on top. Then the hole is concealed.
|
Ah, hah! Good solution so it's not a total loss. Thanks! There is no such thing as a perfect bead, right? Lol.
__________________
Happy Torching! Julie
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
~
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
~
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
~
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
~
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2013-03-16, 9:25pm
|
|
Senior Member
|
|
Join Date: Nov 08, 2010
Location: Bay Area, CA
Posts: 510
|
|
Julie, if you are almost done with the encasing and it is just the tiniest touch of glass I have had luck with cooling the bead a little then using a tight flame to heat just the bit of glass that went too high on the mandrel and plucking it off with a fine pointed tweezer. It is about a 50:50 proposition whether I can pull it off and smooth with the flame as if it never happened or make it worse in which case I keep the bead for me and do what Jacqueline suggested.
Nikki
__________________
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2013-03-17, 5:09am
|
 |
Unmedicated since '62
|
|
Join Date: Jan 18, 2009
Location: Hunter Valley, Australia
Posts: 5,907
|
|
While pushing the glass towards the hole is fine you really have to rely more on the heat. You use the poker to get it part way there then concentrate the heat on the ends to pull the glass into position, that way you'll get nice puckered ends.
__________________
Deb
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
- my 17yo sons first novel
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
- download, get organised, enjoy
|
2013-03-17, 6:19am
|
|
Senior Member
|
|
Join Date: Nov 22, 2012
Location: Eastern Shore Maryland
Posts: 958
|
|
Thank you so much everyone! More practice with Patience as well. I appreciate so much the help. 
__________________
Happy Torching! Julie
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
~
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
~
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
~
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
~
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2013-03-18, 7:07am
|
 |
Redheaded Thread Killer
|
|
Join Date: Sep 18, 2004
Location: Here and There
Posts: 1,922
|
|
Do your beads start off more "round" versus "donut"? If you start off slightly more on the donut shape and head towards more round using heat and gravity, you'll end up with nice puckers without trying to force them. Just sort of heat the glass on one-half of the bead and tilt the mandrel down on that side, then heat and tilt for the other side... and your donut will sort of transition to round and have the nice puckers too.
I hope that made sense...
__________________
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
Currently... torch is cold. Not sure when I'll be making glass again. Hothead and Lynx user.
Nothing on
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2013-03-18, 7:22am
|
|
Senior Member
|
|
Join Date: Nov 22, 2012
Location: Eastern Shore Maryland
Posts: 958
|
|
Quote:
Originally Posted by MistyCherie
Do your beads start off more "round" versus "donut"? If you start off slightly more on the donut shape and head towards more round using heat and gravity, you'll end up with nice puckers without trying to force them. Just sort of heat the glass on one-half of the bead and tilt the mandrel down on that side, then heat and tilt for the other side... and your donut will sort of transition to round and have the nice puckers too.
I hope that made sense...
|
hmmm, yes this is making sense to me. I am usually going donut to round. I think now, I am sometimes forcing the glass too much into my round shaper. Like you said, I need to work more with heat and gravity. Will practice and be patient today and see how it goes. Thank you so much!!
__________________
Happy Torching! Julie
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
~
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
~
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
~
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
~
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2013-03-18, 8:20am
|
|
Senior Member
|
|
Join Date: Jun 12, 2005
Posts: 131
|
|
I've fooled around with making very thin donuts or disks of my encasement color and filling between them with the base color. I was getting bugged by not being able to get ink blue all the way over the white base.
It's another way to tackle the problem.
Nolly
|
|
Currently Active Users Viewing This Thread: 1 (0 members and 1 guests)
|
|
|
Posting Rules
|
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts
HTML code is Off
|
|
|
All times are GMT -7. The time now is 3:59am.
|