I don't think there is any relative site. To do something comparable in boro would go above the limits of most glass kilns. Not to mention the availability and cost of boro flat glass and it's tendency to devitrify at the temps it would need to sit and soak. I've just never heard it done outside of a factory setting, like for cookware. And even that's not really done anymore here.