stringers
I'm pretty new, and I'm having trouble getting the hang of making stringers and wanted to know if it was better to keep trying to make my own stringers or is it ok to buy them?
Thank you
|
2010-06-23, 4:05pm
|
|
Fire Monkey
|
|
Join Date: Jul 01, 2005
Location: at the edge of reason
Posts: 3,264
|
|
If you make them yourself you can control the size.
What's the specific trouble you're having?
__________________
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2010-06-23, 4:08pm
|
Member
|
|
Join Date: Apr 22, 2010
Location: Evansville, Indiana
Posts: 47
|
|
I'm having trouble with them gettting to thin and not very long
|
2010-06-23, 4:15pm
|
|
Fire Monkey
|
|
Join Date: Jul 01, 2005
Location: at the edge of reason
Posts: 3,264
|
|
Here's what I do:
Get a gather (melted glob of glass) at the end of my rod. I make it about the size of a large pea.
Pull the rod out of the flame.
Grab a very small bit of the melty glass with tweezers.
Wait a second for the glass to cool a tiny bit.
Then slowly pull.
If you do it while the glass is too hot you'll get very thin hair-like stringers.
The slower you pull, the fatter the stringer.
It sounds like you might not be heating enough glass and pulling too soon or too fast.
Keep at it. You'll get a feel for it after doing a few.
__________________
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2010-06-23, 4:51pm
|
|
Senior Member
|
|
Join Date: May 21, 2006
Location: Cincinnati
Posts: 2,807
|
|
Making stringer is great practice. I'd recommend keeping at it. Holly's advice is great.
Melt the end of a rod, slowly turning it in your dominant hand to start with. Angle your hand down slightly from the flame (not parallel to your bench). this will allow a small gather of glass to build. When it's about the size of a pea, take the gather out of the flame, pause, and with tweezers, pliers, or the tip of another rod, slowly pull out the molten glass.
The pause is important, especially if you are working soft glass. Otherwise the stringer will be very thin and difficult for a beginner to use.
__________________
Lynda
Cheetah, 5 lpm and 7lpm conc/generator (8-9 psi), natural gas (booster), started 11/06
"The time you enjoy wasting is not wasted time." -- Bertrand Russell
|
2010-06-23, 5:24pm
|
|
Remember to keep smiling
|
|
Join Date: Jul 09, 2009
Location: Texas
Posts: 1,320
|
|
Arrow springs has a tool I use also for my stringers I love it. Called Twisty Tweezers the more glass you grab the thicker your stringer but it is still improtant that you follow the great info Holly & lynda has given you.
Hope this helps. http://www.arrowsprings.com/
__________________
Paula P.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
SRA#P109
|
2010-06-23, 8:15pm
|
|
Lampworkaholic!
|
|
Join Date: Apr 22, 2008
Location: Cornelius, NC - because weather
Posts: 5,158
|
|
Pulling stringer is a basic skill for lampworking. Practice practice practice. It's not that it isn't "OK" to buy stringer. I buy some Commercial Stringer for specific uses. But you will be limited in colors as many colors are not sold in stringer form. Mostly though, It is part of learning heat control and once you "get it" you will have it forever. Good luck!
__________________
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
"And all will turn to silver glass, a light on the water, grey ships pass into the west." Annie Lennox
|
2010-06-23, 8:45pm
|
|
Senior Member
|
|
Join Date: Jul 15, 2009
Location: Ohio
Posts: 2,035
|
|
I still have a hard time with also. But I like being able to do stringer in any color I want. I figure sooner or later something will click (probably later lol) and I will *get* it. In the meantime, skinny stringer can be fun to play with too lol.
__________________
Sonja
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2010-06-23, 9:31pm
|
|
Puddy Cat Lover
|
|
Join Date: Nov 04, 2005
Location: DeMotte, IN
Posts: 1,592
|
|
If you don't want your stringers to be so skinny, try waiting one or two seconds before you pull the glass, and pull slowly. Waiting will allow the glass to stiffen just a bit and your stringer will be thicker. The bigger the melted glob you start with, the longer you can make your stringer. I use pliers to pull mine, but there's so many different ways to do it. Practice practice practice. And don't forget, if your stringers aren't what you'd like them to be, you can always re-melt them back on the rod and start all over again.
J.
__________________
Jeanette Savina Cobb
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. * To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. *
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2010-06-23, 10:28pm
|
|
Fire Monkey
|
|
Join Date: Jul 01, 2005
Location: at the edge of reason
Posts: 3,264
|
|
Quote:
Originally Posted by LyndaJ
Making stringer is great practice. I'd recommend keeping at it. Holly's advice is great.
Melt the end of a rod, slowly turning it in your dominant hand to start with. Angle your hand down slightly from the flame (not parallel to your bench). this will allow a small gather of glass to build. When it's about the size of a pea, take the gather out of the flame, pause, and with tweezers, pliers, or the tip of another rod, slowly pull out the molten glass.
The pause is important, especially if you are working soft glass. Otherwise the stringer will be very thin and difficult for a beginner to use.
|
Much better instructions Lynda!
__________________
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2010-06-24, 4:10am
|
|
Senior Member
|
|
Join Date: Jun 15, 2007
Location: Powell Ohio
Posts: 423
|
|
One thing Loren Stump will tell you is just because it will pull doesn't mean you have to pull. Take your time when you first start pulling when you think you have it the thickness you need . Blow on it and pull slowly and it will stay the same all the way.
|
2010-06-24, 5:10am
|
Linda
|
|
Join Date: Aug 28, 2007
Location: Wasco, IL
Posts: 67
|
|
Corina has a DVD on stringer control which I found to be very helpful. I also purchased a tube of assorted stringers from Frantz so that I could try various colors before purchasing a quarter pound or more of one individual color. Good luck.
Linda
|
2010-06-24, 7:33am
|
|
Senior Member
|
|
Join Date: Jul 03, 2008
Location: Denmark
Posts: 176
|
|
Donīt worry about the length of the stringer.... that will come with practise.
__________________
Lone Ringskaer, Aarhus, Denmark
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. R#115
|
2010-06-24, 8:06am
|
|
Ellyloo-YAH!
|
|
Join Date: Aug 01, 2006
Location: Port Colborne
Posts: 2,775
|
|
It's perfectly ok to buy them if you find stringers you want. They're mostly 'the basics' colours though.
If you have some obscure silver colour that you want a stringer with, you need to know how to pull your own.
Don't worry about waste when you practice, just keep pulling... if it doesn't work, melt it back in! No biggie. White is a good one to practice with...it goes all transparent when TOO runny...
Plus, a stringer doesn't have to be from the END of a rod. You can melt in the middle of a rod, and pull the two pieces apart. The rod then becomes a comfortable handle for the stringer. You can melt shorts together this way, and then pull stringer between them...
__________________
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2010-06-24, 8:10am
|
Member
|
|
Join Date: Apr 22, 2010
Location: Evansville, Indiana
Posts: 47
|
|
Thanks everyone for the great advice, can't wait to give stringers another try. I will keep practice to make them.
Jean Bruce
|
2010-06-25, 9:07am
|
|
Glass-aholic
|
|
Join Date: Mar 21, 2007
Location: CT, tolland CT
Posts: 4,332
|
|
I both buy and make them. It is really nice to buy a mix and get a few colors you may not have, not to mention it saves on time A L O T! I bought a lot of a few colors in stringer, cobalt blue, blue adventurine, ivory, and clear, I might get a few others as i go, but reallly a mix was the best idea, you see what you actually use. When I was on a HH I would do all my encasing with stringer. It was so much easier to get a uniform encasement with commercial pulled stringer.
__________________
Minor 10lpm Oxy-Con + HH on Propylene . . . . . .
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. . To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. hand dyed silk ribbons in many colors!
WASHERS & TOPPERS - layering components for interchangeable glass topper and to use in other jewelry/metalwork.:
|
Currently Active Users Viewing This Thread: 1 (0 members and 1 guests)
|
|
Posting Rules
|
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts
HTML code is Off
|
|
|
All times are GMT -7. The time now is 8:18pm.
|