Default Brass press verses graphite press?

Anyone have any information which is easier to use or makes a better bead. Wanting a heart press and cannot decide which one brass or graphite. I have not tried any graphite presses.
Reply With Quote
  #2  
Old 2017-03-19, 5:07pm
ESC ESC is online now
Senior Member
 
Join Date: Feb 02, 2010
Posts: 1,564
Default

Graphite isn't going to heat up and stick to your glass but it will eventually start to degrade around the edges and is more prone to damage than brass. Graphite is wayyy less expensive than brass. However, if you're not doing production work, I'd go with graphite. I have graphite I've used for almost a decade, doing occasional torching, that's almost as good as new.
__________________
ESC
Soft glass on a Minor/concentrator since 1996
Reply With Quote
  #3  
Old 2017-03-20, 9:59am
Frit Diva's Avatar
Frit Diva Frit Diva is offline
MacGalver
 
Join Date: Oct 15, 2006
Posts: 9,170
Default

I prefer graphite to brass because it is less "grabby". It's hard to explain, but the brass sucks the heat out of the glass so quickly that it kind of feels dead to me after being pressed. It's not something you can see, but there's a feel to it that I personally dislike. Your mileage may vary! Keep in mind, I am one of those people who feels the glass "sigh" sometimes ~ it's just the way my brain works......
__________________
Jo
Frit Diva website http://fritdiva.com
Reply With Quote
  #4  
Old 2017-03-20, 10:06am
Dasi's Avatar
Dasi Dasi is offline
Senior Member
 
Join Date: Aug 27, 2005
Location: Florida
Posts: 2,175
Default

As a press I think brass is more durable. Graphite and brass work differently with glass. Glass slides over graphite without any pulling. Brass grips the glass. For presses this is not a problem as long as it is made well without any undercuts.
__________________
Heather Ferman Web site:www.heatherferman.com
Viking knit End Caps for sale:
http://www.heatherferman.etsy.com
Reply With Quote
  #5  
Old 2017-03-20, 11:34am
Speedslug's Avatar
Speedslug Speedslug is offline
Phill
 
Join Date: Mar 21, 2009
Location: Winnebago, MN
Posts: 1,631
Default

Another thought is that graphite has dozens of various grades and can come in some really poor qualities that would take a good deal of self educating to get knowledgeable on.

Brass only comes in three or four formulations and so can be relied on for getting what you are paying for.


We do have several commercial vendors here that can be depended on here on the LE forum that produce high quality graphite tools.

Graphite is made from carbon and can burn off if exposed to direct flame and is also subject to some wear over time.
Brass has much less of a problem with wear.

Using molds of any sort is going to involve learning heat control in glass and it must also be remembered that molds are more effectively used to 'guide' glass when it is hot enough to be in a plastic state and less as a method of 'forcing' the glass into a form like a glass bottling plant or a molten glass 'hot shop' where liquefied glass is kept in a kiln.
__________________
So, What Do We Do Now?

Last edited by Speedslug; 2017-03-20 at 11:36am.
Reply With Quote
  #6  
Old 2017-03-22, 6:52am
theglasspilcrow's Avatar
theglasspilcrow theglasspilcrow is offline
Member
 
Join Date: Feb 06, 2015
Location: US East Coast
Posts: 43
Default

Personally I prefer brass, especially when I'm working with very stiff glass. Brass seems to retain it's resale value better also, if you aren't sure you're going to love the press.
Reply With Quote
  #7  
Old 2017-03-22, 8:55am
AVTrout's Avatar
AVTrout AVTrout is offline
Bohemian Bead Peddler
 
Join Date: Feb 12, 2007
Location: Lancaster, PA
Posts: 1,173
Default

I don't like brass tools as much as graphite. Brass is too cold. My personal preference.
__________________
Alexis
Reply With Quote
  #8  
Old 2017-03-22, 12:42pm
Lorraine Chandler's Avatar
Lorraine Chandler Lorraine Chandler is offline
Salt Box Beads
 
Join Date: Oct 23, 2005
Location: Heading to Paradise
Posts: 4,073
Default

Prefer graphite here too.
__________________
http://sewvintageuniqueboutique.blogspot.com/
Reply With Quote
  #9  
Old 2017-03-23, 12:04pm
Abacus Beads's Avatar
Abacus Beads Abacus Beads is offline
Senior Member
 
Join Date: Sep 14, 2005
Location: Woodburn, OR
Posts: 1,802
Default

It's graphite for my choice, I have both graphite and brass presses/rollers. I seem to grab the graphite presses before the brass ones when I am working
Liz R
__________________
MADE IN THE U.S.A.

Lead me not into temptation, Oh hell follow me I know a short cut
Reply With Quote
  #10  
Old 2017-03-26, 3:23am
carolinesbeads's Avatar
carolinesbeads carolinesbeads is offline
Senior Member
 
Join Date: Aug 09, 2008
Location: Grand Rapids, MI
Posts: 1,011
Default

I have both as well, I like them both, so far the graphite presses I haven't had any problems with. I usually buy presses based on the shape rather than material. I have one perlenpress graphite press that I really like and use a lot that is not offered in brass.
Reply With Quote
Reply


Currently Active Users Viewing This Thread: 1 (0 members and 1 guests)
 
Thread Tools

Posting Rules
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts

BB code is On
Smilies are On
[IMG] code is On
HTML code is Off
Forum Jump




All times are GMT -7. The time now is 8:24pm.


Powered by vBulletin® Version 3.7.5
Copyright ©2000 - 2017, Jelsoft Enterprises Ltd.
Your IP: 54.167.254.78