Devardi
Has anyone used Divardi glass, and if so, what do you think of it?
Thanks for your input!
|
2014-12-04, 9:24am
|
|
Senior Member
|
|
Join Date: Sep 11, 2014
Location: New Hampshire
Posts: 208
|
|
As a newbie, I use a lot of devardi glass, and even more of their tools, as I simply can't afford many others while I am learning, and they do fine for me.
The glass is very tricky, and for people used to Italian or more expensive glass, it is unworkable. Here is the trick. You must pre warm the rods, if not in a rod warmer, then slowly in the far reaches of the flame. Very slowly!
I think this works for me as a newbie, cause I was afford of heating glass too fast to begin with anyways, so I always introduced it slowly, and with mild fear. Now that I am more accustomed to shocky, and just startled, it doesn't bug me. And like I said. Prewarm it! I have one of their rod warmers sitting on my desk, and I just load it up with what I think I will use that day, turn it on, use other glasses for 20 mins, then away I go.
It does not always mix well with others, but that's the same with many glasses. Lauscha doesn't play well with others, we all learn to just experiment.
Devardi has colors that others don't offer, and they all give a neat organic/recycled look that I simply love.
Yes, it is tricky to work with, stiff and needs to be warmed, but it will always have a place on my bench, and the tools are awesome, in my limited experience, and for the price, simply enable me to do this hobby at all. Without devardi, I would still be using canister gas and second hand graphite hand me downs.
|
2014-12-04, 9:38am
|
Senior Member
|
|
Join Date: May 27, 2008
Location: Albion NY
Posts: 517
|
|
People either tolerate it or hate it.
Its slower to work because of the need to preheat it more.
It can pop if your not careful.
Soft glass is a lot more expencive then boro, but you need a bit more torch.
Divardie has a few colors other suppliers don't.
And its a bit cheeper.
Tools tend to reflect the cost.
Brass prices have dropped a lot so it may start reflecting tool cost in the next few months.
There are a number of suppliers depending on where you are.
__________________
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2014-12-04, 9:41am
|
Senior Member
|
|
Join Date: Dec 31, 2009
Posts: 504
|
|
Beautiful, inexpensive, but surly stuff. They tend to pull their rods very thick and there's a lot of air trapped in them, especially their twistie rods. Pre-warming is essential, or all you'll get is a lot of bench frit. (That's not so bad, actually, because it does work well as frit, particularly in marbles.) Approach their dichroics with care; the last time I bought their dichroic stringers, all the sparkly flaked right off before I even got it near the flame. Their selection of mandrels and their range of tools is very good.
|
2014-12-04, 9:44am
|
|
Queen of the milo field
|
|
Join Date: Jul 30, 2012
Location: In the middle of US and the middle of forty acres
Posts: 1,885
|
|
I don't use the glass, but have bought glass for others who like it, and silver & other metals, frit, etc for me. You can not top their customer service for being quick and courteous no matter if it was your goof up or their mistake.
dj
__________________
Dance all you want, but keep one hand on the wheel.
Sometimes I swim, sometimes I sail, but mostly I just try to stay afloat.
|
2014-12-04, 10:00am
|
|
http://youtu.be/nGt9jAkWi
|
|
Join Date: Oct 23, 2005
Location: Cullman, Alabama
Posts: 2,838
|
|
It's not my first choice of glass. They do have a few colors that are unlike anything else, so I use them. I use it alone because I'm afraid to mix it with other glass. I have a lot of their brass presses & love them because they're unique.
__________________
Vivian
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. - To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2014-12-04, 10:27am
|
Member
|
|
Join Date: Nov 27, 2014
Location: Calgary, AB
Posts: 42
|
|
Thanks so much everyone for your speedy replies. I'm a newbie, so have been checking out different websites etc. Devardi caught my eye because of some of their colours and metal Frits. I'll give some a try, but thanks for the consistent pre-warming advice, otherwise I would have ended up with just piles of frit
|
2014-12-04, 1:21pm
|
|
Bigger, longer, and uncut
|
|
Join Date: Aug 01, 2007
Location: Fort Collins, CO
Posts: 447
|
|
Indeed, either heat VERY slowly in the flame or get some sort of rod warmer. (I used a curling iron heater/oven from Sally Beauty Supply.)
Some of the blues devitrify terribly for me. The one rod I really like is the black. It doesn't sparkle and pit when reheated. I used it as the base for lots of my beads.
__________________
Evelyn
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2014-12-04, 3:01pm
|
|
Shelarious
|
|
Join Date: Jul 18, 2007
Location: Cincinnati, OH
Posts: 1,953
|
|
I think they have some really gorgeous colors, but I also think that if you are a beginner, you will want to go explore other options. I wouldn't want you discouraged by popping glass and getting burned. I like the stiffness to it, and the opals are pretty, and the price is right, but it's seriously moody.
__________________
~Shelley
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2014-12-04, 4:24pm
|
|
JennyD
|
|
Join Date: Oct 24, 2013
Location: San Jose, California
Posts: 421
|
|
You either love or hate it, that is what I have learned.
I am too inpatient to wait for it to warm up so I don't use the glass. I did start off with it though. Their tools are pretty good and inexpensive and as someone else mentioned, their customer service is GREAT!
__________________
JennyD
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. ...I'd rather be beading!
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2014-12-04, 6:22pm
|
|
honorary bead lady
|
|
Join Date: Jan 14, 2008
Location: Mostly the doghouse
Posts: 5,180
|
|
Asking about Devardi is like asking which clear is best, it usually results in an us vs them type thread and can get pretty heated
__________________
David To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2014-12-04, 9:38pm
|
Member
|
|
Join Date: Nov 27, 2014
Location: Calgary, AB
Posts: 42
|
|
Quote:
Originally Posted by houptdavid
Asking about Devardi is like asking which clear is best, it usually results in an us vs them type thread and can get pretty heated
|
So, are you an "us" or a "than"
|
2014-12-04, 9:38pm
|
Member
|
|
Join Date: Nov 27, 2014
Location: Calgary, AB
Posts: 42
|
|
Oops. A "them"?
|
2014-12-04, 11:27pm
|
Naysayer
|
|
Join Date: Sep 22, 2009
Posts: 1,203
|
|
I like their tools, although myself and someone else got a marble mold where the graphite smelled so strongly of fuel we had to toss them. I've tried a couple of colors, like the metallic silver one, it's nice but like others said you have to preheat, I just stick one end into the kiln.
What colors do people suggest, those that are not in the other palettes...and, how are their purple & pinks? I heard one pink was not compatible but heck if I can remember which one.
|
2014-12-05, 1:43pm
|
|
Slogan Challenged...
|
|
Join Date: Mar 21, 2009
Location: Maricopa, Arizona
Posts: 6,287
|
|
The rose one wasn't, although I don't recall if it was the med or the dark
Gorgeous colors, I wish they were easier to use. I'd love to see if the smaller 4-6 mm rods work any better. Until then, I just get the tools and misc. stuff from them. Tools work fine and the customer service is great.
Just depends on what you need, I guess. It's not expensive to try a few things and find out if you can work like that.
__________________
Kristin ~
Facebook: To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
Etsy: To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2014-12-05, 1:59pm
|
|
Senior Member
|
|
Join Date: Sep 11, 2014
Location: New Hampshire
Posts: 208
|
|
I love the luscious pink, and the bi-color rods. They are all really big, but I pull them down into stringers, and it's fast easy and really pretty! The transparent purple over opaque lilac is my favorite!
The flat encasing strips are kind of fun, but not as clear as I had hoped, but good if I take my time.
|
2014-12-05, 2:21pm
|
|
http://youtu.be/nGt9jAkWi
|
|
Join Date: Oct 23, 2005
Location: Cullman, Alabama
Posts: 2,838
|
|
I got some of their dichro strips & wasn't happy with them at all.
__________________
Vivian
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. - To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2014-12-05, 4:34pm
|
|
Senior Member
|
|
Join Date: Jun 11, 2005
Location: SUNNY FLORIDA~West Coast!
Posts: 9,423
|
|
Quote:
Originally Posted by Khaleesi Dane
As a newbie, I use a lot of devardi glass, and even more of their tools, as I simply can't afford many others while I am learning, and they do fine for me.
The glass is very tricky, and for people used to Italian or more expensive glass, it is unworkable. Here is the trick. You must pre warm the rods, if not in a rod warmer, then slowly in the far reaches of the flame. Very slowly!
I think this works for me as a newbie, cause I was afford of heating glass too fast to begin with anyways, so I always introduced it slowly, and with mild fear. Now that I am more accustomed to shocky, and just startled, it doesn't bug me. And like I said. Prewarm it! I have one of their rod warmers sitting on my desk, and I just load it up with what I think I will use that day, turn it on, use other glasses for 20 mins, then away I go.
It does not always mix well with others, but that's the same with many glasses. Lauscha doesn't play well with others, we all learn to just experiment.
Devardi has colors that others don't offer, and they all give a neat organic/recycled look that I simply love.
Yes, it is tricky to work with, stiff and needs to be warmed, but it will always have a place on my bench, and the tools are awesome, in my limited experience, and for the price, simply enable me to do this hobby at all. Without devardi, I would still be using canister gas and second hand graphite hand me downs.
|
Excuse me. Have you ever even used Lauscha or did that comment come from Devardi??
??
__________________
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
Still North America's Largest Lauscha Dealer!
Now reopened in South Florida!!
Like US on Facebook ! To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2014-12-05, 5:47pm
|
Senior Member
|
|
Join Date: Apr 08, 2010
Location: The warmer half of MN
Posts: 155
|
|
Yep, Devardi discussions tend get heated fast, and there's your evidence. the tools are cheap but functional, and I love their flower presses! And with a rod warmer, the glass is quite functional. Great for learning on.most people do tend to move on to better glass if they stick with beadmaking. But there are several colors they have that you can't get elsewhere.
|
2014-12-05, 6:26pm
|
|
Slogan Challenged...
|
|
Join Date: Mar 21, 2009
Location: Maricopa, Arizona
Posts: 6,287
|
|
I can't believe they came out with flower presses, great price too.
I agree many start with it, but it's very frustrating and may be discouraging to new folks. I would say get some experience, then come try it for the colors and see if there are some you don't mind working with,
__________________
Kristin ~
Facebook: To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
Etsy: To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2014-12-05, 6:37pm
|
Senior Member
|
|
Join Date: Apr 08, 2011
Location: NC
Posts: 1,687
|
|
Their families of pinks and peaches can't be beat for colors. I just have to remember to preheat them, and they're fine.......and cheap, too!
__________________
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
Barbara
|
2014-12-05, 8:03pm
|
|
Senior Member
|
|
Join Date: Sep 11, 2014
Location: New Hampshire
Posts: 208
|
|
No offense Paula D. Actually I got it from your own website, and from using the few lauscha rods I know I have, cause they are labeled. Your site describes a very specific annealing schedule that I can't attain as yet, since I don't have a digital annealer.
My statement was not 'lauscha is bad', it was simply that not all glasses play well together.
Pretty fair statement. I like the lauscha I have, but I am saving the rest of it until I have a better kiln. No point wasting it now, is there?
I like the lauscha colors, and lord knows it is easy to handle, I just can't afford that quality to learn on. It's like giving a 16 yr old a Ferrari to drive to school!
|
2014-12-05, 8:53pm
|
|
http://youtu.be/nGt9jAkWi
|
|
Join Date: Oct 23, 2005
Location: Cullman, Alabama
Posts: 2,838
|
|
[ I got 3 but haven't played with them much. I'll post pics when I get some done QUOTE=KJohn;4686093]I can't believe they came out with flower presses, great price too.
I agree many start with it, but it's very frustrating and may be discouraging to new folks. I would say get some experience, then come try it for the colors and see if there are some you don't mind working with,[/quote]
__________________
Vivian
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. - To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2014-12-06, 12:48am
|
Junior Member
|
|
Join Date: Dec 04, 2014
Posts: 1
|
|
I use Devardi and I only starting in Oct and had never used anything else.. So I am a beginner but to be honest the glass never turned me off. It is a stiff glass and does shocke easily but you just have to have the patience and time . I have prob ordered 15 different color's from them and I find they are great. But that's just what I think. I do have the rod warmer which makes it that much easier and I find they mix fine together I enjoy Devardi color's as well they all seem to work well with each other
|
2014-12-06, 10:17am
|
|
Senior Member
|
|
Join Date: Jun 11, 2005
Location: SUNNY FLORIDA~West Coast!
Posts: 9,423
|
|
Quote:
Originally Posted by Khaleesi Dane
No offense Paula D. Actually I got it from your own website, and from using the few lauscha rods I know I have, cause they are labeled. Your site describes a very specific annealing schedule that I can't attain as yet, since I don't have a digital annealer.
My statement was not 'lauscha is bad', it was simply that not all glasses play well together.
Pretty fair statement. I like the lauscha I have, but I am saving the rest of it until I have a better kiln. No point wasting it now, is there?
I like the lauscha colors, and lord knows it is easy to handle, I just can't afford that quality to learn on. It's like giving a 16 yr old a Ferrari to drive to school!
|
I hope you do get to try Lauscha someday with an annealer as it is beautiful glass. You are correct. It does not work well for many without being annealed. It does mix well with almost everything if you reheat your bead before putting it into the annealer and us the annealing schedule. That incompatibility rumor has been going around for a long time and it hurts a lot of innocent people (such as the people that work at Lauscha). And keeps people from trying a nice brand of glass.
__________________
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
Still North America's Largest Lauscha Dealer!
Now reopened in South Florida!!
Like US on Facebook ! To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2014-12-06, 10:38am
|
|
Senior Member
|
|
Join Date: Sep 11, 2014
Location: New Hampshire
Posts: 208
|
|
Quote:
Originally Posted by PaulaD
I hope you do get to try Lauscha someday with an annealer as it is beautiful glass. You are correct. It does not work well for many without being annealed. It does mix well with almost everything if you reheat your bead before putting it into the annealer and us the annealing schedule. That incompatibility rumor has been going around for a long time and it hurts a lot of innocent people (such as the people that work at Lauscha). And keeps people from trying a nice brand of glass.
|
Oh, I intend to, in fact I have several rods of it and double helix that I am saving for that time when I can do it justice! I was drooling at your site just the other day, cause I am having horrible issues with the clear I have, but I just can't accurately anneal it yet. (Pout pout ). When I have my beehive annealer paid for, you better have some awesome stock on hand!! Cause I'm coming your way!
|
2014-12-06, 10:53am
|
Junior Member
|
|
Join Date: Feb 09, 2014
Posts: 1
|
|
Love it!
I personally bought their big start up kit to get started with lampwork! It included torch, tools, and pretty much everything I needed. I like the glass if only for the reason that it has taught me patience I tend to rush things when I'm trying anything artsy so I can just see the finished product, and this has FORCED me to slow down or else I won't get anywhere. I find that it all works quite nicely for me
|
2014-12-06, 2:11pm
|
|
Borovangelist
|
|
Join Date: Jan 26, 2007
Location: Auburn, MA
Posts: 3,002
|
|
I've seen perfectly competent beadmakers wrestle with some lauscha colors being incompatible, so there is some issue there despite what the lauscha distributor with a vested financial interest wants to tell you. It happens depending how often folks want to say something along the lines of, 'you're just not working it right.'
If a glass is that finicky it's not usually worth the hassle.
As for devardi, it's cheap enough to try. If you like it, great. If not, now you know. At least it's not 50-100.00 a pound to find out.
I'm all for working any glass you can find, you never know when you'll find something new that you love.
__________________
-Tom
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. | To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. | To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2014-12-06, 3:12pm
|
|
Brainy McSmartypants
|
|
Join Date: Jul 19, 2005
Location: Claypool, IN
Posts: 581
|
|
Devardi is shrapnel in rod form unless you really preheat it. They do have some LOVELY colors, but I find that many of the opaques devit. And I won't mix it with any other glass after the problems I had with some really nice focals with Devardi surface work... when the Devardi popped off (and I'm not a newbie, they were melted in just fine).
As for Lauscha, I'd have to keep a spreadsheet next to my torch with a compatibility list- don't encase this, or use this to encase, don't use this color with this color, this one's ok with that but not with that. And at over $20 a pound for decidedly pretty colors and nice clear, I end up tossing probably 25% of my pieces because I don't want to have to reprogram my kiln for their exclusive annealing schedule to make the glass "work for me". I have to do far too much work for IT to get it to work. Silver glass, pressed? Ha! Never with Lauscha, and do not even think of mixing Tangerine, which is a LUSCIOUS orange over or under anything. I can't even get it to not crack under Zephyr clear and that stuff plays with EVERYTHING.
As a beginner, I second that thought that you would be better coming back to Devardi later after some time learning how to control the glass when introducing it. I would hate to see someone turned off of glass work by being pelted with hot glass constantly (avoid CIM for that, too, mostly) and cracks. Start off with some nice easy to play with Effetre and then move onto the more experimental stuff
__________________
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
Amy K
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2014-12-06, 3:14pm
|
|
Smile, it's contagious!
|
|
Join Date: Oct 31, 2005
Location: Location: Location
Posts: 4,938
|
|
what in the hell are you doing here?
ETA: this post was directed at Amy.
__________________
Squid says I'm a special kind of Bithc. To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
Some people are like a Slinky... not really good for anything, but you still can't help but smile when you shove them down the stairs.
|
Currently Active Users Viewing This Thread: 1 (0 members and 1 guests)
|
|
Posting Rules
|
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts
HTML code is Off
|
|
|
All times are GMT -7. The time now is 3:55am.
|